| Model |
Name |
Cylinder Opening Ratio
（V/V） |
Characteristic & Purpose |
Operating Temperature
（℃）
|
Time
(min) |
| HAR-101 |
Room-temperature zinc series phosphating solution |
5% |
Used in soaking process of anti-rust steel bottom |
15-50 |
5-20 |
| HAR-101S |
Room-temperature zinc series phosphating solution |
5% |
Used in spraying process of anti-rust steel bottom |
15-50 |
2-5 |
| HAR-102 |
Room-temperature zinc series phosphating solution |
5% |
Used in soaking process for cold-plastic lubrication and corrosion protection of steel |
65-85 |
5-10 |
| HAR-103 |
Medium-temperature zinc series phosphating solution |
10% |
Used in soaking process of anti-rust steel bottom and deformation processing |
60-70 |
5-8 |
| HAR-104 |
Medium-temperature zinc/calcium series phosphating solution |
5% |
Used in soaking process of anti-rust steel bottom |
10-60 |
3-5 |
| HAR-104S |
Medium-temperature zinc/calcium series phosphating solution |
5% |
Used in spraying process of anti-rust steel bottom |
10-60 |
1-2 |
| HAR-105 |
Room-temperature iron series phosphating solution |
5% |
Used in soaking process of film treatment before aluminum or aluminum alloy coating |
10-35 |
2-5 |
| HAR-105S |
Room-temperature iron series phosphating solution |
5% |
Used in spraying process of film treatment before aluminum or aluminum alloy coating |
10-35 |
1-3 |
| HAR-106 |
Room-temperature iron series phosphating solution |
5% |
Used in soaking process of film treatment before electroplating of zinc plate or zinc alloy |
10-50 |
5-10 |
| HAR-106S |
Room-temperature iron series phosphating solution |
5% |
Used in spraying process of film treatment before electroplating of zinc plate or zinc alloy |
10-50 |
2-5 |
| HAR-108 |
Accelerant |
0.5% |
Used with HAR-101, HAR-102 and HAR-106 |
10-50 |
5-10 |
| HAR-108S |
Accelerant |
0.2% |
Used with HAR-101S and HAR-106S |
10-50 |
2-5 |
| Model |
Name |
Characteristic & Purpose |
Cylinder Opening (G/L) |
Operating Conditions |
Time
(min) |
| HAR-201 |
Room-temperature degreasing powder |
Steel, iron, copper and zinc alloy degreasing and dewaxing agent |
40-60 |
15-70℃ impregnation method |
5-20 |
| HAR-202 |
Medium-temperature degreasing powder |
Applicable to degreasing of steel, iron, copper and other metals |
50-80 |
60-90℃ soaking method |
3-5 |
| HAR-203 |
Ultrasonic degreasing powder |
Applicable to degreasing of steel and zinc alloy |
80-100 |
60-90℃ hot-dip ultrasonic treatment |
3-5 |
| HAR-204 |
Steel component degreasing powder |
Application to degreasing and dewaxing of steel components |
40-60 |
15-70℃ soaking method |
3-15 |
| HAR-204S |
Steel component degreasing powder |
Application to degreasing and dewaxing of steel components |
40-60 |
15-50℃ spraying method |
2-5 |
| HAR-205 |
Steel component electrolysis degreasing powder |
Applicable to electrolysis degreasing and dewaxing of steel cathodes and anodes |
50-80 |
60-90℃4-10A/d㎡ |
1-2 |
| HAR-206 |
Zinc alloy degreasing powder |
Degreasing and dewaxing of zinc alloy and copper alloy |
40-60 |
15-70℃ hot-dipping method |
5-10 |
| HAR-206S |
Zinc alloy degreasing powder |
Degreasing and dewaxing of zinc alloy and copper alloy |
40-60 |
15-70℃ spraying process |
2-5 |
| HAR-207 |
Zinc alloy electrolysis degreasing powder |
Applicable to degreasing of zinc and copper cathodes & steel cathodes and anodes |
50-80 |
50-70℃2-6A/d㎡ |
0.5-2 |
| HAR-208 |
Neutral degreasing agent |
Degreasing of steel, copper, zinc and aluminum alloy |
10-30 |
Room-temperature or medium-temperature soaking process |
3-15 |
| HAR-208S |
Degreasing additive |
Degreasing of steel, copper, zinc and aluminum alloy |
10-30 |
Room-temperature or medium-temperature spraying process |
3-5 |
| HAR-209 |
Acidic degreasing agent |
Degreasing and oxide removal of copper and aluminum alloy |
30-50 |
Room-temperature soaking |
3-5 |
| HAR-210 |
Cold release agent |
Degreasing of various metal or mechanical parts |
100-200 |
Room-temperature soaking |
3-5 |
| HAR-211 |
Emulsion degreasing agent |
Degreasing and dewaxing of metal or mechanical parts |
20-30 |
Room-temperature soaking |
5-10 |
| HAR-212 |
Degreasing surfactant |
Applicable to degreasing of various metals |
20-30 |
Room-temperature or medium-temperature soaking |
5-10 |
| HAR-214 |
Defoaming agent |
Used for defoaming in degreasing process |
0.1-0.5 |
Room-temperature or medium-temperature soaking or spraying |
0.5-1 |
| HAR-215 |
Defoaming agent |
Used for defoaming in degreasing process |
0.5-1.0 |
Room-temperature or medium-temperature soaking or spraying |
0.5-1 |
| Model |
Name |
Characteristic & Purpose |
Operating Conditions |
Time
(min) |
| HAR-301A |
Paint remover |
Used for paint removal of defective steel workpiece after liquid coating |
Room-temperature raw liquid soaking |
1-5 |
| HAR-301B |
Paint remover |
Applicable to various powder coatings for steel, non-stick pans, etc. |
Room-temperature raw liquid soaking |
5-15 |
| HAR-302 |
Paint remover |
Applicable to defective zinc and aluminum products after coating |
Room-temperature raw liquid soaking |
5-10 |
| HAR-303 |
Passivation agent |
To improve the corrosion resistance of film |
Room-temperature slotting of 3-5% |
0.5-1 |
| HAR-304 |
Anti-rust powder |
To improve the anti-rust performance of rust removal procedures |
Room-temperature slotting of 3-5% |
2-3 |
| HAR-305 |
Room-temperature steel blackening agent |
Applicable to room-temperature steel blackening into film |
Diluted 5 times above 5℃ |
2-3 |
| HAR-306 |
Neutralizing agent |
Used for neutralization of residual or free acid on workpiece surface |
Room-temperature soaking or spraying, slot opening of 3-5% |
1-2 |
| HAR-307 |
Mist inhibitor |
Used for inhibition of acid mist in anti-rust pickling process |
Add 0.1-0.5% at room temperature |
0.5-1 |
| HAR-308 |
Rust remover |
To remove rust of steel workpiece |
Room-temperature soaking, slot opening of 20-50% |
Depending on the situation |
| HAR-309 |
Adhesive peptide conditioning agent |
Surface activity adjustment before phosphating |
Room-temperature soaking or spraying, 0.1-0.3% |
1-2 |
| HAR-309A |
Adhesive peptide conditioning agent |
Surface activity adjustment before phosphating |
Room-temperature soaking or spraying, 0.2-0.5% |
1-2 |
| HAR-310 |
Rust removal and prevention solution |
To remove and prevent rust |
Soaking or removal of raw solution |
Depending on the situation |
| HAR-311 |
Surface conditioning agent |
Surface adjustment before steel phosphating |
Room-temperature soaking, slot opening of 2-3% |
2-3 |
| Model |
Name |
Characteristic & Purpose |
Slotting Ratio
（G/G） |
Operating Temperature
（℃） |
Time
(min) |
| HAR-68A |
Vitrification agent |
Treatment of steel and zinc/aluminum alloy before soaking or spraying |
2-3% |
0℃-50℃ |
0.5-2.0 |
| HAR-68G |
Vitrification agent |
Treatment of steel and zinc/aluminum alloy before soaking or spraying |
2-3% |
0℃-50℃ |
0.5-2.0 |
| HAR-68GS |
Vitrification agent |
Treatment of steel and zinc/aluminum alloy before soaking or spraying |
1-2% |
0℃-50℃ |
0.5-2.0 |
| HAR-68A2 |
Vitrification agent |
Treatment of steel and zinc/aluminum alloy before soaking or spraying |
3-5% |
0℃-50℃ |
0.5-2.0 |
| HAR-68A3 |
Vitrification agent |
Treatment of steel and zinc/aluminum alloy before soaking or spraying |
5-7% |
0℃-50℃ |
0.5-2.0 |
| HAR-68AD |
Vitrification agent |
Treatment of steel and zinc/aluminum alloy before soaking or spraying |
0.1-0.2% |
0℃-50℃ |
0.5-2.0 |
| HAR-6804 |
Degreasing agent |
Treatment of steel component before soaking and spraying |
3-5% |
15℃-70℃ |
2.0-15.0 |
| HAR-6804A |
Degreasing agent |
Treatment of steel component before soaking and spraying |
4-6% |
15℃-70℃ |
2.0-15.0 |
| HAR-6804B |
Degreasing agent |
Treatment of steel and zinc/aluminum alloy before soaking or spraying |
5-10% |
15℃-50℃ |
2.0-15.0 |
| HAR-6804G |
Degreasing agent |
Treatment of steel before soaking or spraying |
2-5% |
15℃-70℃ |
2.0-15.0 |
| HAR-6804GS |
Degreasing agent |
Treatment of steel before soaking or spraying |
2-3% |
15℃-70℃ |
2.0-15.0 |
| HAR-6808 |
Degreasing aid |
Treatment of steel before soaking or spraying |
3-10% |
15℃-70℃ |
2.0-15.0 |
| HAR-6808A |
Degreasing aid |
Treatment of steel and zinc/aluminum alloy before soaking or spraying |
3-10% |
15℃-70℃ |
2.0-15.0 |
| HAR-6808B |
Degreasing aid |
Treatment of steel and zinc/aluminum alloy before soaking |
3-10% |
15℃-70℃ |
2.0-15.0 |
| HAR-6808G |
Degreasing aid |
Treatment of steel before soaking or spraying |
0.2-0.5% |
15℃-70℃ |
2.0-15.0 |
| HAR-6808GS |
Degreasing aid |
Treatment of steel before soaking or spraying |
1-2% |
15℃-70℃ |
2.0-15.0 |
| HAR-68H |
Alkalinity regulator |
Treatment of steel and zinc/aluminum alloy before soaking |
0.1-0.2% |
0℃-50℃ |
0.5-2.0 |
| HAR-680H |
Alkalinity regulator |
Treatment of steel and zinc/aluminum alloy before soaking |
0.1-0.2% |
0℃-50℃ |
0.5-2.0 |
| HAR-680HG |
Alkalinity regulator |
Treatment of steel and zinc/aluminum alloy before soaking |
0.1-0.2% |
0℃-50℃ |
0.5-2.0 |
| HAR-680HGS |
Alkalinity regulator |
Treatment of steel and zinc/aluminum alloy before soaking
|
0.1-0.2% |
0℃-50℃ |
0.5-2.0 |